ASTM A106 Pipa Baja Karbon Bulat Bulat

dapatkan harga terbaru

Jenis pembayaran:	L/C,T/T,D/P
Inkoterm:	FOB,CFR,CIF,EXW
Transportasi:	Ocean,Land,Express
Pelabuhan:	Tianjin,Qingdao,Shanghai

Hubungi sekarang

Deskripsi Produk

Atribut Produk

Model No: ASTM A106

Standar: ASTM, bs, GB, JIS, API

Bahan: Q195-Q345, 10 # -45 #, A53-A369, ST35-ST52

Bentuk Bagian: Bulat

Tempat Asal: Cina

Aplikasi: Pipa Fluida, Pipa Boiler, Pipa gas, PIPA MINYAK, Pipa Struktur

Proses Produksi: Hot Rolled

Sertifikasi: ce, API

Tabung Khusus: Pipa API, Pipa Dinding Tebal

Apakah Paduan: Non-Paduan

Toleransi: ± 1%

Kategori: Pipa Baja Seamless

Layanan Pengolahan: Pembengkokan, Pengelasan, Meninju, Pemotongan, Dekorasi

Length: 6-12m

Ketebalan: customized

Material: Seamless Steel

& pengiriman paket

Menjual unit	:	Ton
Tipe paket	:	Standar kemasan yang diekspor
Contoh pada gamba	:

The file is encrypted. Please fill in the following information to continue accessing it

ASTM A53 A106 Pipa Baja Bulat Karbon Bulir

Pipa baja karbon berdinding tebal



Deskripsi Produk

Pipa baja yang mulus adalah bagian tubular atau silinder berongga, biasanya tetapi tidak harus dari penampang melingkar, terutama digunakan untuk menyampaikan zat yang dapat mengalir - cairan dan gas (cairan), bubur, bubuk dan massa padatan kecil.

Proses deformasi pipa baja yang digulung panas dapat diringkas sebagai tiga tahap: ekstensi, perforasi, dan finishing. Pipa-pipa baja panas yang digulung panas relatif terhadap rolling dingin yang terguling dingin di bawah suhu rekristalisasi dari rolling dan hot rolled dilakukan di atas suhu rekristalisasi bergulir. Pipa baja mulus yang digulung panas dapat merusak penyempurnaan butiran kristal baja, cor mikrostruktur baja ingot dan menghilangkan cacat struktur mikro sehingga organisasi baja yang memadatkan, meningkatkan sifat mekanik. Peningkatan ini tercermin dalam arah bergulir sehingga baja tidak lagi pada tingkat tertentu isotropik; Tuangkan pembentukan gelembung, retakan dan osteoporosis, di bawah tekanan dan suhu tinggi juga dapat dilas bersama.

Pipa baja yang digulung panas (tabung mulus) dalam berbagai ukuran, spesifikasi, nilai & ketebalan sesuai kebutuhan klien. Kisaran yang ditawarkan oleh tabung tersedia sesuai standar internasional & nasional dan dapat tersedia dari kami dengan harga terjangkau. Pipa -pipa ini digunakan di berbagai industri aplikasi seperti pembuatan kapal, pembangkit listrik, minyak dan gas, otomotif, pabrik gula dan penyulingan, industri semen dan konstruksi dll.

ASTM A106 Pipa tekanan mulus (juga dikenal sebagai ASME Sa106 Pipe) umumnya digunakan dalam konstruksi kilang minyak dan gas, pembangkit listrik, pembangkit petrokimia, boiler, dan kapal di mana perpipaan harus mengangkut cairan dan gas yang menunjukkan suhu dan tingkat tekanan yang lebih tinggi .

perkenalan produk

ASTM A106 Pipa mulus (juga dikenal sebagai pipa ASME SA106) biasanya digunakan dalam pembangunan kilang minyak dan gas, pembangkit listrik, pembangkit petrokimia, boiler dan kapal. Pipa -pipa ini harus membawa cairan yang menunjukkan tingkat suhu dan tekanan yang lebih tinggi.

Tentang ASTM A106 gr b
ASTM A106 Gr . B Pipa mulus (juga dikenal sebagai ASME SA106 GR B Pipes) adalah pipa nominal pipa CS yang mulus untuk penggunaan suhu tinggi. Komposisi kimia dari 106 gr.b adalah sebagai berikut:
C≤0.25 , Mn = 0,27-0.93 , p≤0.035 , S≤0.035 , Si≤0.1 , Cr≤0.4 , Cu≤0.4 , sifat mekanik: ób≥415 / MPa, Ós≥240 / MPa.
Tentang ASTM A106 gr c
ASTM A106 Gr . Pipa C Seamless (juga dikenal sebagai ASME SA106 GR C Pipes) adalah pipa baja karbon-mangan untuk boiler berdiameter besar suhu tinggi dan superheater. Komposisi kimianya sederhana dan mirip dengan baja karbon 20g, tetapi kandungan karbon dan mangannya lebih tinggi, sehingga kekuatan luluh sekitar 12% lebih tinggi dari 20g, dan plastisitas dan ketangguhannya tidak buruk. Baja ini memiliki proses produksi yang sederhana dan kemampuan kerja dingin dan panas yang baik. Menggunakannya untuk mengganti header 20g (economizer, dinding air, superheater suhu rendah dan header reheater) dapat mengurangi ketebalan dinding sekitar 10%, yang dapat menghemat biaya material, mengurangi beban kerja pengelasan, dan meningkatkan header perbedaan stres saat start-up .

Data teknis

Persyaratan kimia ASTM A106 Grade A, B dan C

Grade	Grade A	Grade B	Grade C
Carbon max. %	0.25	0.30	0.35
Manganese %	0.27 to 0.93	0.29 to 1.06	0.29 to 1.06
Phosphorous, max. %	0.035	0.035	0.035
Sulfur, max. %	0.035	0.035	0.035
Silicon, min.%	0.10	0.10	0.10
Chrome, max. %	0.40	0.40	0.40
Copper, max. %	0.40	0.40	0.40
Molybdenum, max. %	0.15	0.15	0.15
Nickel, max. %	0.40	0.40	0.40
Vanadium, max.%	0.08	0.08	0.08

Catatan: Total Cr, Cu, Mo, Ni, dan V tidak boleh melebihi 1%

Persyaratan tarik ASTM A106 Grade A, B dan C.

Grade	Grade A	Grade B	Grade C
Tensile Strength, min., psi	48000	60000	70000
Yield Strength, min., psi	30000	35000	40000

Sifat mekanik dari ASTM A106 Pipes Seamless

ASTM A106 Steel Grade	Tensile Test MPa or N/mm2
ASTM A106 Steel Grade	Min. Yield Point	Min. Tensile Strength	Elongation (%)
Grade A	205	330	20
Grade B	240	415	20
Grade C	275	485	20

Setara dengan pipa astm A106 yang mulus

Specification	Mechanical Properties	Grade A	Grade B	Grade C
ASTM A53	Tensile strength, min, psi (MPa)	48000(330)	60000(415)
ASTM A53	Yield strength, min, psi (MPa)	30000(205)	35000(240)
ASTM A106	Tensile strength, min, psi (MPa)	48000(330)	60000(415)	70000(485)
ASTM A106	Yield strength, min, psi (MPa)	30000(205)	35000(240)	40000(275)

Persyaratan manufaktur & pengujian untuk pipa mulus A106

Heat Treatment	Hot-finished pipe need not be heat treated. Cold-drawn pipe shall be heat treated after the final cold draw pass at a temperature of 1200 °F (650 °C) or higher.
Process	The steel shall be killed steel, with the primary melting process being open-hearth, basic-oxygen, or electric-furnace, possibly combined with separate degassing or refining. If secondary melting, using electroslag remelting or vacuum-arc remelting is subsequently employed, the heat shall be defined as all of the ingots remelted from a single primary heat. Steel cast in ingots or strand cast is permissible. When steels of different grades are sequentially strand cast, identifi- cation of the resultant transition material is required. The producer shall remove the transition material by any estab- lished procedure that positively separates the grades.
Surface Treatment	Oil-dip, Varnish, Passivation, Phosphating, Shot Blasting
Hydrostatic Testing	Inspection test pressures produce a stress in the pipe wall equal to 60% of specified minimum yield strength (SMYS) at room temperature. Maximum Pressures are not to exceed 2500 psi for NPS3 and must stay under 2800 psi for the larger sizes. Pressure is maintained for not less than 5 seconds.
Nondestructive Electric Test	The full body of each pipe shall be tested with a nondestructive electric test in accordance with Practice E 213, E 309, or E 570.
Mechanical Tests Specified	Tensile Test — NPS 8 and larger — either transverse or longitudinal acceptable smaller than NPS 8 — weighed in lots. Larger sizes — by length. Flattening Test — NPS 2-1/2 and larger. Bending Test (Cold) — NPS 2 and under.

Seamless Steel Pipe

Aplikasi

Pipa dan tabung baja karbon digunakan dalam kondisi tekanan tinggi. Mereka sangat tahan terhadap guncangan dan getaran, membuatnya ideal untuk mengangkut cairan. Pipa baja karbon banyak digunakan di sejumlah industri, seperti bahan konstruksi, buidling, jembatan, mengangkut air dan limbah, industri minyak dan gas, tabung boiler dan kondensor, aplikasi bertekanan tinggi, dan pemrosesan kimia.

- Bahan onstruksi / jembatan

- Mengangkut air dan limbah

- Industri minyak dan gas

- Tabung boiler dan kondensor

- Aplikasi bertekanan tinggi

- Pemrosesan Kimia

Pengemasan dan Transportasi

1) Kemasan: 3 lapisan pengemasan. Di dalamnya adalah kertas kerajinan, tengah adalah film plastik air dan lembaran baja GI di luar untuk ditutupi oleh strip baja dengan kunci, dengan lengan koil dalam atau sebagai persyaratan pelanggan.

2) Pengiriman: Kami memiliki kerja sama jangka panjang dengan banyak perusahaan pelayaran berpengalaman dan akan menemukan moda transportasi yang paling cocok untuk Anda.

3) Ketentuan Perdagangan: FOB/CIF/CFR

4) Pelabuhan Pengiriman: Qingdao/Tianjin/Shanghai

5) Pengiriman: A: Panjang: ≤6m, dimuat dalam wadah 20gp. B: Panjang: ≤12m, dimuat dalam wadah 40gp.

Komentar: ukuran wadah 20gp (di dalam: 5898*2352*2393mm); Ukuran wadah 40gp (di dalam: 12032*2352*2393mm); Ukuran wadah 40HQ (di dalam: 12032*2352*2698mm).

6) Waktu Pengiriman: Ukuran Normal: 7-15 hari Kirim dari gudang secara langsung. Ukuran Khusus: 15-30 hari dibuat khusus untuk Anda.